Journal: RSC Advances

Article Title: Anisotropic growth of gas–liquid precipitated ceria mesocrystals to wires several micrometers in length

doi: 10.1039/c8ra05362f

Figure Lengend Snippet: XRD patterns of the CeO 2 nanoparticles prepared by the gas–liquid precipitation process under various conditions using Ce(NO 3 ) 3 solution (a) at 25 °C for 3 days, (b) at 25 °C for 10 days, (c) at 7 °C for 3 days, (d) at 60 °C for 3 days, and using a CeCl 3 solution (e) at 60 °C for 3 days without the initial pH adjustment, and (f) at 60 °C for 3 days with the initial pH adjustment to pH 4.6 using HCl.

Article Snippet: Aqueous NH 3 (Wako Pure Chemical Industries, Ltd., Japan, 40 mL, 28 wt%) was used as the NH 3 gas generating solution.

Techniques:

Journal: RSC Advances

Article Title: Anisotropic growth of gas–liquid precipitated ceria mesocrystals to wires several micrometers in length

doi: 10.1039/c8ra05362f

Figure Lengend Snippet: SEM images of the ceria nanoparticles prepared by the gas–liquid precipitation process under various condition using Ce(NO 3 ) 3 solution (a) at 25 °C for 3 days, (b) at 25 °C for 10 days, (c) at 7 °C for 3 days, (d) at 60 °C for 3 days, and using a CeCl 3 solution (e) at 60 °C for 3 days without the initial pH adjustment, and (f) at 60 °C for 3 days with the initial pH adjustment to pH 4.6 using HCl.

Article Snippet: Aqueous NH 3 (Wako Pure Chemical Industries, Ltd., Japan, 40 mL, 28 wt%) was used as the NH 3 gas generating solution.

Techniques:

Journal: RSC Advances

Article Title: Anisotropic growth of gas–liquid precipitated ceria mesocrystals to wires several micrometers in length

doi: 10.1039/c8ra05362f

Figure Lengend Snippet: Change in pH of the starting material (Ce(NO 3 ) 3 ) solution at 60 °C for various times. Each pH was measured at 25 °C after cooling.

Article Snippet: Aqueous NH 3 (Wako Pure Chemical Industries, Ltd., Japan, 40 mL, 28 wt%) was used as the NH 3 gas generating solution.

Techniques:

Journal: RSC Advances

Article Title: Anisotropic growth of gas–liquid precipitated ceria mesocrystals to wires several micrometers in length

doi: 10.1039/c8ra05362f

Figure Lengend Snippet: TEM images and FFT analyses results of the CeO 2 nanoparticles prepared by the gas–liquid precipitation process for various durations using Ce(NO 3 ) 3 at 60 °C for (a) 10 min, (b) 2 h, (c) 8 h, and (d) 3 days.

Article Snippet: Aqueous NH 3 (Wako Pure Chemical Industries, Ltd., Japan, 40 mL, 28 wt%) was used as the NH 3 gas generating solution.

Techniques: